Active Ingredient Content: | Al2O3 |
Application: | Chemical Industry,Medicine |
Still deciding? Get samples of US$ 10/kg
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
According to the different AL2O3 content of inert alumina porcelain balls, filler porcelain balls are divided into: ordinary porcelain balls, inert alumina porcelain balls, aluminum porcelain balls, high aluminum porcelain balls, 99 high aluminum porcelain balls, convex and concave grooving porcelain balls, active porcelain balls, open porcelain balls, microporous porcelain balls, thermal storage porcelain balls.
Name | Ceramic ball | 23-30%AL203 Ceramic ball | Medium alumina ceramic ball | High alumina ceramic ball | 99-Alumina ceramic ball |
Al203+SiO2(%) | >93 | >92 | >93 | >94 | >99 |
Al203(%) | 17-23 | 23-30 | 40-75% | 85-97 | 99 |
Fe203(%) | <1 | <1 | <1 | <1 | 0.2 |
Ca0(%) | <0.5 | <1.5 | <1.5 | <0.5 | 0.2 |
MgO(%) | <0.5 | <1.5 | <0.5 | <0.5 | 0.1 |
K2O+Na20(%) | <4 | <4 | <3.5 | <4 | >0.5 |
TiO2 | <0.5 | ≤0.5 | <0.1 | <0.1 | 0.5 |
Leachable Fe203 |
<0.1 | <0.1 | <0.005 | <0.001 | |
water adsorption | <0.5% | <0.5% | <1 | <2 | 2-5 |
grain density g/cm3 |
2.3-2.4 | 2.3-2.4 | 2.6-2.9 | 3.4 | 3.2-3.6 |
operation temp(max).C | 980 | 980 | 1450 | 1580 | 1580 |
Moh's hardness | >6.5 | >7 | >7 | >7.5 | >7.5 |
compressive strength | KN/Particle | ||||
φ6mm | >0.5 | >0.5 | >0.50 | >0.6 | >1 |
φ25mm | >6.5 | >6.5 | >4.9 | >55 | >8 |
φ38mm | >8.9 | >8.9 | >5.5 | >54 | >8 |
φ50mm | >9 | >9.8 | >6.5 | >7.8 | >15 |