CAS No.: | 1344-28-1 |
---|---|
Formula: | Al203 |
EINECS: | 236-675-5 |
Material: | Ceramic |
Structure Feature: | Ball Shape |
Type: | Random Packing |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
name | 17%-19%ceramic ball | |||||||||
minimum content(%) | max content(%) | ordinary content(%) | ||||||||
chemical component | AL203 | 17 | 19 | 18 | ||||||
SiO2 | 70 | 77 | 74.9 | |||||||
AL203+SiO2 | 90 | 94 | 93 | |||||||
Fe203 | / | 1 | 0.5 | |||||||
TiO2 | / | 0.5 | 0.46 | |||||||
CaO | / | 0.5 | 0.42 | |||||||
MgO | / | 0.5 | 0.38 | |||||||
Na20 | / | 2 | 1.12 | |||||||
K20 | / | 3.5 | 3.28 | |||||||
leachable iron(%) | ≤0.1 | |||||||||
apparent porosity | diameter≥10mm | ≤0.4 | ||||||||
diameter=6mm | ≤1.0 | |||||||||
diameter=3mm | ≤3.0 | |||||||||
water adsorption(%) | acid fastness(%) | alkali resistance(%) | specific bulk weight (g/cm3) |
Bulk density(kg/cm3) | Moh's hardness | |||||
<2.0 | >90 | >85 | 1.3-1.35 | 2300 | >6.5 | |||||
heat conductivity coefficient (w/m2.k) |
specific heat capacity (J/kg.ºC) |
operation temp max(ºC) | thermal expansivity (%) (500ºC) | thermal shock resistance(500ºC To cold water) |
||||||
0,9-1.0 | 628-837 | 1050 | 0.2 | ten times | ||||||
geometrical features | Specification ( mm ) | 3 | 6 | 10 | 13 | 16 | 19 | 25 | 38 | 50 |
Minimum compressive strength | ≥0.3 | ≥0.8 | ≥1.0 | ≥2.5 | ≥3.2 | ≥7.4 | ≥8.3 | ≥9.3 | ≥15.4 |